Calcium Aluminate CaO 49-54% Al2O3:40-45% Sio2:2.8% max Size:5-25mm 90% m Calcium AluminateCaO49-54%Al2O340-45%Sio22.8% maxTio22.7% maxMgO2.0% maxFe2O31.5% maxMelting Point1380 deg CParticle size5-25 mm   90% minPre-fused clinker for refined steel-making is newly...

Castable Dense Cast Low Cement Base on Tublaralum Sinter GT-90 Castable Dense Cast Low Cement Base on Tublaralum Sinter GT-90Technical data sheetBrandGT-90Max service temp.(°C)1800Bulk density(g/cm3)3.00Chemical composition(%)Al2O393.0 MinSiO25.0 MaxCaO1.5 MaxFe2O30.1MaxCold...

Dense Refractory Castable for circulation fluidized bed boiler(CFBC castable) Refractory low cement castable for boiler Dense Refractory Castable for circulation fluidized bed boiler(CFBC castable)BrandGT-30service temperature °C1800°CChemical composition(%)Al2O394%...

Fused Silica is manufactured from deliberated silica sand,through high termperature fusion,cooling,smash and selecting. Fused SilicaFused Silica is manufactured from deliberated silica sand,through high termperature fusion,cooling,smash and selecting,the appearance is colorless...

Premium Alumina Dense Castable have very high strength, use temperature:1790 deg c. very low Fe2O3:0.2% max low CaO:2.0%max BrandGT-20Max service temp.(°C)1800Bulk density(g/cm3)3.00 minChemical composition(%)Al2O394 minCaO2.0 maxFe2O30.2 maxModulus of rupture(...

Non-crystalline of calcium aluminate ALuminous Aggregate is a synthetic calcium aluminate aggregate. Non-crystalline of calcium aluminateALuminous Aggregate is a synthetic calcium aluminate aggregate manufactured by the fusion of bauxite and limestone into a partially...

dry ramming mass dry ramming massTechnical data sheetBrandAM-85Max service temp.(°C)1800Chemical composition(%)Al2O389.28MgO9.40SiO20.22Fe2O30.08CaO0.19Cold crush strength(Mpa)1500°C×3h31Apparent porosity %27.1Methood of installationrammingmain usemelting steel in...

High Alumina Castable Low Cement LC-160 High Alumina Castable Low Cement LC-160 Technical data sheetBrandLC-160Max service temp.(°C)1750Bulk density(g/cm3)2.7Chemical composition(%)Al2O378SiO215-18Fe2O31.0 MaxCaO1.5 MaxCold crush...

Dry Ramming mass for melting steel in Induction furnaces and Middle Frequency Ramming material Rammed lining Dry ramming mass Dry Ramming mass for melting steel in Induction furnaces and Middle FrequencyTechnical data sheetBrandDE-86Max service temp.(°C)1800Bulk...

Silex; Silica SiO2: 99.13% Alumina Al2O3: 0.36% grain size: 0-5mm use: clean the melting iron Silex;Chemical analysisSilica SiO2: 99.13%Alumina Al2O3: 0.36%Iron Oxyde Fe2O3: 0.18%Magnesia MgO: 0.04%Lime CaO: 0.09%grain size: 0-5mmuse: clean the melting iron  ...